SiC/Cr-Al-Si/glass multilayer oxidation resistant coating for carbon/carbon composites

Multilayer oxidation resistant SiC/Cr-Al-Si/glass coating for C/C composites was prepared by a three step method of pack cementation, plasma spraying and slurry dipping. The phase composition, microstructure and oxidation resistance of multilayer SiC/Cr-Al-Si/glass coating were studied by XRD, SEM and isothermal oxidation test at 1773 K in air respectively. Double layer SiC/Cr-Al-Si coating consisting of Al 3·21 Cr 0·47 , Cr 3 Si and Al 2 O 3 can protect C/C composites from oxidation for only 61 h due to its high porosity. When a layer of borosilicate glass doped with MoSi 2 was coated on the surface of the as sprayed Cr-Al-Si coating, multilayers of SiC/Cr-Al-Si/glass coating were formed such that they can protect C/C composites from oxidation for 95 h with only 5·3% weight loss and the corresponding weight loss rate is only 0·92×10 −4 g cm −2 h −1 . The positive effect of the borosilicate glass coating on the oxidation resistance of the coating may be attributed to its own fluidity at high temperature.