The Role of Wafer Edge in Wafer Bonding Technologies

Semiconductor Wafer Bonding is a key process step for many technologies such as engineered substrates (SOI and cavity SOI Wafers) MEMS (sensors, microfluidics), 3D integration (device stacking) and wafer thinning (temporary wafer bonding). Almost all publications in the field of wafer bonding are concerned with how bonding is working and can be performed at the actual wafer area. It is also well known that any disturbances on the wafer surface, such as particles, scratches, areas with increased surface roughness, or steps from the wafer processing act in most of the wafer bonding technologies as points of discontinuities with negative influences on the bonding behavior (generation of voids, non-hermeticity, reduced bonding strength). Due to the general geometry of the wafers and their defined sizes they have an edge. This wafer edge has special properties and also acts as an area of discontinuities. Even in well-established wafer bonding techniques, which allow close to perfect bonding of the wafer area, at the wafer edge there are smaller or wider unbonded areas. In particular, in industrial production processes, these unbonded areas are often the cause of process problems in the process steps after wafer bonding. For example, wet chemicals can be tapped in such unbonded areas and become released later into other tools, parts of the poorly bonded wafer edge can flake off, and in the grinding process wafers can break due to missing mechanical support at unbonded edge areas. The reasons for these unbonded areas can originate in different process areas such as the raw wafer manufacturing (here the wafer edge is initially defined), in the wafer processing before bonding (for every process step the wafer edge is a zone of discontinuities with special effects and inhomogeneities), in the bonding process (here the bonding needs to be formed until the very edge of the wafer) and in the process steps after the wafer bonding (bonded wafer edges can be easily damaged). In the proposed paper the influence of wafer edge effects on different wafer bonding technologies, such as direct, anodic and glass frit bonding, will be discussed, and improvements will be described. In this abstract, only one short example will be given: Semiconductor wafer bonding is used to process cavity SOI-Wafers to allow the advantageous production of absolute pressure sensors. Here, two kinds of wafers, which later become the pressure sensor membrane by grinding and polishing, have to be bond