Angle-Resolved Photoelectron Spectroscopy Studies of Initial Stage of Oxidation on C-Face 4H-SiC

The practical use of power devices that use SiC has already been reported. However, performance of a SiC MOSFET has not reached the level predicted based on the physical properties of SiC. One of the reasons is that interface state density (D it ) at SiO 2 /SiC is more than an order of magnitude higher than that at SiO 2 /Si. Therefore, the reduction of the D it is important for device performance improvement. Many studies have been performed to reveal the origin of D it . [1] Also some types of interface defects have been identified, such as carbon clusters, Si/C dangling bonds, and silicon oxycarbides (SiO x C y ) species. [2] However, the chemical structure of the interface transition region still remains unclear, resulting in the insufficient understanding of the origin of D it and the atomic structure of SiO 2 /SiC interface. Therefore, it is possible to reveal the formation process of SiO 2 /SiC interface structure by oxidation, to control the interface structure on the basis of the knowledge, the key for improving the performance of the SiC MOSFET. In this paper, we report the results of an examination of the changes in chemical bonding state of SiO 2 /SiC structure with the progress of thermal oxidation using angle-resolved X-ray photoelectron spectroscopy (AR-XPS). 4H-SiC C-face epitaxial films with 4° off-oriented were used in this study. The samples were prepared as follows. The sample was cleaned in the mixture of H 2 SO 4 and H 2 O 2 (H 2 SO 4 :H 2 O 2 =4:1) at 80-85 ºC, and the native oxide was removed by dipping in 5% hydrofluoric acid (HF) followed by a rinse in deionized water. The sample was oxidized at 800 °C in dry oxygen with a pressure of 133 Pa. Then, the sample was oxidized in dry oxygen with a pressure of 133 Pa at 850 °C. The Si 2 p , O 1 s and C 1 s photoelectron spectra, excited by monochromatic AlKα radiation, were measured at a photoelectron take-off angle of 15 and 90 ° with an energy resolution of 0.37 eV and an acceptance angle of 3.3 °, using an ESCA-300 manufactured by Scienta Instruments AB [3]. Figures 1 (a) and (b) show Si 2 p and C 1 s photoelectron spectra arising from the sample, respectively. Here, these spectra are normalized by Si 2 p and C 1 s photoelectron intensity arising from SiC substrate. Figures 1 (c), (d) and (e) show the decomposed Si 2 p 3/2 and C 1 s spectra, respectively. As seen in Fig. 1 (a), the oxide increases with the increase of oxidation time. As seen in Fig. 1 (b), components present in the u