Thermal stability of proton conducting acid doped polybenzimidazole in simulated fuel cell environments

Recently, polybenzimidazole membrane doped with phosphoric acid (PBI) was found to have promising properties for use as a polymer electrolyte in a high temperature (ca. 150 to 200 C) proton exchange membrane direct methanol fuel cell. However, operation at 200 C in strongly reducing and oxidizing environments introduces concerns of the thermal stability of the polymer electrolyte. To simulate the conditions in a high temperature fuel cell, PBI samples were loaded with fuel cell grade platinum black, doped with ca. 480 mole percent phosphoric acid (i.e., 4.8 H{sub 3}PO{sub 4} molecules per PBI repeat unit) and heated under atmospheres of either nitrogen, 5% hydrogen, or air in a thermal gravimetric analyzer. The products of decomposition were taken directly into a mass spectrometer for identification. In all cases weight loss below 400 C was found to be due to loss of water. Judging from the results of these tests, the thermal stability of PBI is more than adequate for use as a polymer electrolyte in a high temperature fuel cell.