Blue Electroluminescence in SrSO 4 :Ce-Based Thin-Films

A blue electroluminescence (EL) device was fabricated using SrSO 4 :Ce-based phosphor layers deposited by rf sputtering in Ar–H 2 S atmosphere. Peak emission wavelength was observed at 420 nm corresponding to the energy transition from the T 2g (5d) level to the F 5/2 (4f) level of Ce ions. This wav...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Japanese Journal of Applied Physics 1998-07, Vol.37 (7R), p.3992
Hauptverfasser: Morishita, Takashi, Ichii, Akira, Matsui, Masahiro, Tonomura, Shoichiro, Konishi, Tokuzo
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:A blue electroluminescence (EL) device was fabricated using SrSO 4 :Ce-based phosphor layers deposited by rf sputtering in Ar–H 2 S atmosphere. Peak emission wavelength was observed at 420 nm corresponding to the energy transition from the T 2g (5d) level to the F 5/2 (4f) level of Ce ions. This wavelength is shorter than any previously reported, which suggests that the energy state of the excited 5d electrons is sensitive to the crystal field surrounding Ce ions. A high-resolution two-crystal X-ray fluorescence spectrometer (HRXRF) was used to examine the composition of the SrSO 4 -based phosphor layers and chemical state of Ce ions in them. The chemical state of Ce ions was primarily 3+ in the blue-green emitting phosphor layers, which were mainly composed of SrS. An increase in SrSO 4 concentration in the phosphor layers leads to a change in the chemical state of Ce ions, resulting in a blue shift in EL emission. A constant high luminance of 5 cd/m 2 was obtained under 5 KHz sinusoidal driving. The transferred charge density of the SrSO 4 :Ce-based EL device was found out to be fairly low compared to the conventional SrS:Ce EL device.
ISSN:0021-4922
1347-4065
DOI:10.1143/JJAP.37.3992