Fabrication of ordered Au nanodot arrays utilizing anodic aluminum oxide templates formed on Si substrate
The authors have fabricated Au nanodot arrays using anodic aluminum oxide (AAO). Two types of AAO, namely, hexagonal and matrix pores, were used as a template for Au deposition. Au nanodots with a controlled size between 20 and 80 nm were obtained by changing the pore size in the AAO template. AAO t...
Gespeichert in:
Veröffentlicht in: | Journal of vacuum science & technology. B, Microelectronics and nanometer structures processing, measurement and phenomena Microelectronics and nanometer structures processing, measurement and phenomena, 2011-05, Vol.29 (3), p.031805-031805-7 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The authors have fabricated Au nanodot arrays using anodic aluminum oxide (AAO). Two types of AAO, namely, hexagonal and matrix pores, were used as a template for Au deposition. Au nanodots with a controlled size between 20 and 80 nm were obtained by changing the pore size in the AAO template. AAO templates of 200 nm thick were fabricated using two-step anodization. Al films of 150 nm thick grown on Si (100) substrates were indented using the nanoimprint method prior to the anodization for the matrix array of AAO. In addition, for smaller size pores, neutral beam etching was used to remove the barrier layer. The pore size was extracted from the image analysis to the images obtained by field emission secondary electron microscopy. |
---|---|
ISSN: | 1071-1023 2166-2746 1520-8567 2166-2754 |
DOI: | 10.1116/1.3592431 |