Structural characterization of Fe-N films prepared by laser ablation
Fe-N films were deposited on glass substrates at temperatures between 20 and 250/spl deg/C in a wide range of nitrogen pressure by KrF excimer laser ablation. Magnetic properties of the Fe-N films are discussed associated with the film structure. Saturation magnetization over 2000 emu/cm/sup 3/ with...
Gespeichert in:
Veröffentlicht in: | IEEE transactions on magnetics 1995-11, Vol.31 (6), p.3850-3852 |
---|---|
Hauptverfasser: | , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext bestellen |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Fe-N films were deposited on glass substrates at temperatures between 20 and 250/spl deg/C in a wide range of nitrogen pressure by KrF excimer laser ablation. Magnetic properties of the Fe-N films are discussed associated with the film structure. Saturation magnetization over 2000 emu/cm/sup 3/ with a decreased coercivity is observed in bct Fe-N films with high crystal orientation prepared at a substrate temperature of 250/spl deg/C. |
---|---|
ISSN: | 0018-9464 1941-0069 |
DOI: | 10.1109/20.489793 |