Superconducting current leads of YBCO and Pb-BSCCO

The authors fabricated and measured cylindrical superconducting current leads composed of a Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub 7/ (YBCO) and Bi/sub 2-x/Pb/sub x/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub 10/ (Pb-BSCCO) that were approximately 20 cm long and 1 cm/sup 2/ in cross section. A steady-state, DC, criti...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers); (United States) 1991-03, Vol.27 (2), p.1854-1857
Hauptverfasser: Gubser, D.U., Miller, M.M., Toth, L., Rayne, R., Lawrence, S., Alford, N.M., Buttons, T.W.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext bestellen
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The authors fabricated and measured cylindrical superconducting current leads composed of a Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub 7/ (YBCO) and Bi/sub 2-x/Pb/sub x/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub 10/ (Pb-BSCCO) that were approximately 20 cm long and 1 cm/sup 2/ in cross section. A steady-state, DC, critical current of 170 (230) A at a temperature of 77 K was measured for YBCO (Pb-BSCCO) using a voltage criterion of 2*10/sup -7/ V ( rho =8*10/sup -10/ Omega -cm). This current was limited by the current-induced self-magnetic field. At a temperature of 63 K this current increased to approximately 390 (465) A. The character of the magnetic field dependence of the critical current and shape of the current-induced voltage curves are different for the two materials.
ISSN:0018-9464
1941-0069
DOI:10.1109/20.133557