Transmission electron microscopy and electron diffraction study of the short-range ordering structure of α-LiFeO 2

The basic structure of α -LiFeO 2 , lithium iron oxide, is a cubic NaCl-type structure with a lattice constant of 0.42 nm; some short-range ordering characterized by octahedral clusters exists. The local structure of the short-range ordering was investigated by transmission electron microscopy and electron diffraction. A new short-range ordering structure was found in local areas. The local structure has a cubic lattice with a doubled lattice constant. The occupation factors of cations on Wyckoff sites 4( a ) and 4( b ) are different from those on 24( d ) sites, but the stoichiometric composition in cubic clusters is the same as the macroscopic composition. The number of pairs in which iron cations exist in nearest-neighbor sites and next nearest-neighbor sites is reduced in the structure. This means that a magnetic interaction between the iron cations is reduced by cation ordering even without spin ordering at room temperature.