Using the ferroelectric/ferroelastic effect at cryogenic temperatures for set-and-hold actuation

The ferroelectric and ferroelastic properties of lead-zirconate-titanate (PZT) based stack actuators have been characterized at temperatures down to 25 K and under various levels of constant compressive stress. Experiments indicate that the coercive field and magnitude of strain at the coercive field display an inverse relationship with temperature. A factor of 5.5 increase in coercive field, and a factor of 4.3 increase in strain is observed at 25 K in comparison to the room-temperature conditions. This information was used to induce non-180° domain wall motion in the material through the application of electric fields at or near the coercive field. The change in remanent strain accompanying these effects was shown to increase in magnitude as temperature decreased, reaching values of 2000 ppm at 25 K. This behavior was also shown to be temporally stable even under compressive loads. Additionally, it was demonstrated that the material can be returned to its original strain state through a repolarizing electric field. This switchable behavior could be exploited for future set-and-hold type actuators operating at cryogenic temperatures.