Molecular dynamics simulations of ultrafast radiation induced melting at metal–semiconductor interfaces

Metal–semiconductor contacts in silicon carbide (SiC) diodes endure damages at the interface when exposed to harsh radiation environments. Due to the rapid rise in temperature and ultrafast cooling that follows the radiation impact, the structural properties of the materials can be altered through m...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 2021-06, Vol.129 (21)
Hauptverfasser: Ravichandran, Ashwin, Mehta, Mohit, Woodworth, Andrew Allan, Lawson, John W
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Metal–semiconductor contacts in silicon carbide (SiC) diodes endure damages at the interface when exposed to harsh radiation environments. Due to the rapid rise in temperature and ultrafast cooling that follows the radiation impact, the structural properties of the materials can be altered through melting, recrystallization, and amorphization. A detailed understanding of the material failure modes at the interface is lacking, specifically at the nanoscale. We use molecular simulations to investigate the ultrafast melting at tungsten (W)–SiC interfaces following radiation damage and apply deep learning techniques to track the transient evolution of the local molecular structures. We show that W near the radiation track undergoes melting and, eventually, most of it recrystallizes with a noticeable degree of undercooling, while SiC is rendered permanently amorphous. The observation of local undercooling in W films is important as it can affect the device performance even before the bulk melting temperature of the material is reached. We also show that at high temperatures, the interface undergoes a fracture-like failure. The results presented here are significant in understating the different failure modes of SiC diode materials.
ISSN:0021-8979
1089-7550
DOI:10.1063/5.0045766