Heterointerface stability in GaAs-on-Si grown by metalorganic chemical vapor deposition
The stability of the electrical and structural properties of GaAs directly deposited on Si by metalorganic chemical vapor deposition is examined. Extended annealing at 900 °C leads to substantial diffusion of Si across the heterointerface while under the same conditions there is no significant motio...
Gespeichert in:
Veröffentlicht in: | Applied physics letters 1987-08, Vol.51 (9), p.682-684 |
---|---|
Hauptverfasser: | , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The stability of the electrical and structural properties of GaAs directly deposited on Si by metalorganic chemical vapor deposition is examined. Extended annealing at 900 °C leads to substantial diffusion of Si across the heterointerface while under the same conditions there is no significant motion of Si incorporated as a dopant into the GaAs surface region. The degree of enhancement of Si diffusion ranges from a factor of ∼250 for 0.5-μm-thick GaAs films to ∼5 for 4-μm-thick films. The annealing time and GaAs layer thickness dependence of Si diffusivity near the interface is consistent with a defect-modulated mechanism. A large fraction of this mobile Si is electrically inactive. |
---|---|
ISSN: | 0003-6951 1077-3118 |
DOI: | 10.1063/1.98333 |