Effect of Gd substitution on the structural, magnetic, and magnetocaloric properties of HoCrO3

Rare-earth chromites are a new type of magnetoelectric multiferroics. In this work, a Ho0.33Gd0.67CrO3 powder sample was synthesized via a citrate route, and the structural properties were characterized by X-ray diffraction, scanning electron microscopy, and the Raman technique. The UV-Visible optic...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 2018-02, Vol.123 (5)
Hauptverfasser: Yin, Shiqi, Zhong, Wei, Guild, Curtis J., Shi, Jianhang, Suib, Steven L., Cótica, Luiz Fernando, Jain, Menka
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Rare-earth chromites are a new type of magnetoelectric multiferroics. In this work, a Ho0.33Gd0.67CrO3 powder sample was synthesized via a citrate route, and the structural properties were characterized by X-ray diffraction, scanning electron microscopy, and the Raman technique. The UV-Visible optical absorbance spectra were also measured in the wavelength range of 200–800 nm. The valence state of Cr was found to be purely 3+ according to the X-ray photoelectron spectroscopy. The temperature-dependent dielectric constant and loss tangent data measured between the frequencies of 1 kHz and 1 MHz show no anomalies around the magnetic transition temperature of the material. The dc magnetization measurements show that the ordering temperature of Cr3+ ( TNCr) is 155 K for Ho0.33Gd0.67CrO3, which is larger than 140 K for HoCrO3. The positive slope of the Arrott plots from 0 T to 7 T reveals that the antiferromagnetic-paramagnetic phase transition is second-order in nature. At a field of 7 T, the Ho0.33Gd0.67CrO3 sample showed a giant magnetocaloric entropy change, −ΔS, of ∼23.3 J/kg K at 5 K, and a refrigeration capacity of ∼481.2 J/kg, which are much higher than those of pure bulk HoCrO3. This renders this material prospective for magnetic refrigeration in the low temperature (
ISSN:0021-8979
1089-7550
DOI:10.1063/1.5003637