Lithium-ion conducting La2/3− x Li3 x TiO3 solid electrolyte thin films with stepped and terraced surfaces

La2/3−xLi3xTiO3 (LLT, x = 0.1 and 0.167) thin films were grown on (001)-oriented SrTiO3 (STO) substrates by pulsed laser deposition. The resultant LLT films were heteroepitaxially grown with atomically flat surfaces. Although the films considered to be single crystalline, they were composed of 90°-rotated multi domains (∼5 nm in size) with epitaxial relationships of (100) [001] LLT || (001) [100] STO and (100) [010] LLT || (001) [100] STO. The bulk conductivity of the LLT (x = 0.1) films was 2.5 × 10−2 S cm−1 at 190 °C, comparable to that of a bulk single crystalline LLT. Single crystalline LLT thin films with atomically flat surfaces should help clarify interfacial lithium-ion conductivity. At the request of the authors, this article is being retracted effective 1 March 2013.