Ultraviolet photoelectron spectroscopy of poly(pyridine-2,5-diyl), poly(2,2′-bipyridine-5,5′-diyl), and their K-doped states

Ultraviolet photoelectron spectra were measured using synchrotron radiation for two kinds of π-conjugated polymers, poly(pyridine-2,5-diyl) (PPy) and poly(2,2′-bipyridine-5,5′-diyl) (PBPy) which exhibit n-type electrically conducting properties. The two compounds show similar spectra and they were a...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:The Journal of chemical physics 1995-08, Vol.103 (7), p.2738-2744
Hauptverfasser: Miyamae, Takayuki, Yoshimura, Daisuke, Ishii, Hisao, Ouchi, Yukio, Seki, Kazuhiko, Miyazaki, Takafumi, Koike, Tsuneaki, Yamamoto, Takakazu
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Ultraviolet photoelectron spectra were measured using synchrotron radiation for two kinds of π-conjugated polymers, poly(pyridine-2,5-diyl) (PPy) and poly(2,2′-bipyridine-5,5′-diyl) (PBPy) which exhibit n-type electrically conducting properties. The two compounds show similar spectra and they were analyzed with MO calculations and the comparison with the data of related molecules. The ionization threshold energies of PPy and PBPy were found to be 6.3 and 6.35 eV, respectively. These values are higher than those of π-conjugated conducting polymers capable of p doping. Upon potassium doping of PBPy, two new states appeared in the originally empty energy gap and the intensity of the state at 0.65 eV from EF grows as the doping proceeds. This finding and the change of optical absorption spectra upon doping indicate that bipolaron bands are formed in K-doped PBPy. While K-doped PPy also shows similar gap states, it requires higher dopant concentration to create bipolaron bands than in the case of K-doped PBPy. The difference of the dependence on dopant concentration between K-doped PPy and K-doped PBPy is discussed based on the conformational difference between these polymers.
ISSN:0021-9606
1089-7690
DOI:10.1063/1.470508