Magnetoresistance and Hall effect of chromium dioxide epitaxial thin films

Epitaxial CrO2 thin films have been grown on TiO2(100) and Al2O3(0001) substrates by atmospheric pressure chemical vapor deposition. The films have a Curie temperature (Tc) of around 393 K with the ones grown on TiO2 exhibiting in-plane uniaxial magnetic anisotropy. They also display metallic charac...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 1999-04, Vol.85 (8), p.5585-5587
Hauptverfasser: Li, X. W., Gupta, A., McGuire, T. R., Duncombe, P. R., Xiao, Gang
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Epitaxial CrO2 thin films have been grown on TiO2(100) and Al2O3(0001) substrates by atmospheric pressure chemical vapor deposition. The films have a Curie temperature (Tc) of around 393 K with the ones grown on TiO2 exhibiting in-plane uniaxial magnetic anisotropy. They also display metallic characteristics, with room temperature resistivity of about 285 μΩ cm, dropping by about two orders of magnitude upon cooling down to 5 K. Magnetoresistance (MR) properties of the films have been measured with the magnetic field in the plane. For a field of 40 kOe, a positive transverse MR of about 25% at 5 K and a negative MR of about 7% at near Tc have been observed. In addition, Hall resistivity has been measured with magnetic field up to 40 kOe. A positive ordinary Hall effect is found at low temperatures, indicating the conduction carriers are holes.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.369807