Stability of Zn doping profile in modulation-doped multiple quantum well structure

Stability of the Zn doping profile in InGaAs/InGaAsP modulation-doped multiple quantum well (MD-MQW) structures grown by low-pressure metalorganic vapor-phase epitaxy (MOVPE) has been investigated by secondary ion mass spectrometry and transmission electron microscope with wedge-shaped samples. Alth...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 1996-08, Vol.80 (3), p.1405-1413
Hauptverfasser: Otsuka, Nobuyuki, Ishino, Masato, Matsui, Yasushi
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Stability of the Zn doping profile in InGaAs/InGaAsP modulation-doped multiple quantum well (MD-MQW) structures grown by low-pressure metalorganic vapor-phase epitaxy (MOVPE) has been investigated by secondary ion mass spectrometry and transmission electron microscope with wedge-shaped samples. Although excellent stability of Zn profile is confirmed in an as-grown sample with modulation doping (d=3 nm CZn=1×1018 cm−3), the modulation-doping structure diminishes after the second epitaxial regrowth of a p-InP layer (CZn=1×1018 cm−3) carried out by either liquid phase epitaxy or MOVPE, which is applicable for buried heterostructure lasers. However, the modulation-doping profile is successfully preserved even after regrowth of the p-InP layer for 90 min in a sample constructed of an undoped InP clad layer instead of a p-InP clad layer superposed on the MD-MQW layers. A Zn diffusion coefficient in the modulation-doped region is extremely small, having a value of less than 7×10−18 cm2/s. The maximum Zn concentration in the modulation-doped region in barrier layers was found to be 2×1018 cm−3 for obtaining a stable modulation-doping structure. It is proposed that the suppression of both interstitial Zn atoms and subsequently produced interstitial group III atoms, which are generated in the p-InP clad layer via a kick-out mechanism and diffuse into the MD-MQW region, is important for preserving modulation-doping structure.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.363029