Effect of the CoFe2O4 thin film thickness on multiferroic property of (00l)-oriented Pb(Zr0.5Ti0.5)O3∕CoFe2O4∕Pb(Zr0.5Ti0.5)O3 trilayer structure
In this study, we have fabricated (00l)-oriented Pb(Zr0.5Ti0.5)O3∕CoFe2O4∕Pb(Zr0.5Ti0.5)O3 (PZT/CFO/PZT) trilayer thin films on LaNiO3 coated substrates by dual-cathode rf sputtering system. The thicknesses of top and bottom PZT thin films were fixed at 100nm but those of the CFO interlayer were 40,...
Gespeichert in:
Veröffentlicht in: | Journal of applied physics 2008-04, Vol.103 (7) |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | In this study, we have fabricated (00l)-oriented Pb(Zr0.5Ti0.5)O3∕CoFe2O4∕Pb(Zr0.5Ti0.5)O3 (PZT/CFO/PZT) trilayer thin films on LaNiO3 coated substrates by dual-cathode rf sputtering system. The thicknesses of top and bottom PZT thin films were fixed at 100nm but those of the CFO interlayer were 40, 80, and 120nm, respectively. The x-ray diffraction showed well-defined PZT and CFO peaks with (00l) orientation, and large grains with columnar structure were observed by field-emission scanning electron microscopy. Hard-magnetic M-H loop with a saturation magnetization of ∼235emu∕cm3 and ferroelectric hysteresis curve with saturation polarization of ∼40.1μC∕cm2 were measured at room temperature for the PZT/CFO (120 nm)/PZT trilayer thin films. Due to the low-resistance CFO interlayer in series with the PZT layers, the ferroelectric property does not significantly vary with the CFO interlayer thickness. In contrast, the possibility of the existence of nonmagnetic interfacial layer at the CFO/PZT interface causes the reduction of the magnetization. Both of the good magnetic and ferroelectric responses suggest that the (00l)-oriented PZT/CFO/PZT trilayer thin film is a promising magnetoeletric material for study. |
---|---|
ISSN: | 0021-8979 1089-7550 |
DOI: | 10.1063/1.2839313 |