Touching the properties of NbTi by carbon doped tapes with mechanically alloyed MgB2
Combining mechanical alloying and powder-in-tube processing is a promising way to obtain tapes with excellent properties. Taking advantage of the properties of nanocrystalline precursor powders, it was possible to obtain Jc values of 104A∕cm2 at 12.1T and 4.2K. Evidential substitution of carbon into...
Gespeichert in:
Veröffentlicht in: | Applied physics letters 2007-08, Vol.91 (8) |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Combining mechanical alloying and powder-in-tube processing is a promising way to obtain tapes with excellent properties. Taking advantage of the properties of nanocrystalline precursor powders, it was possible to obtain Jc values of 104A∕cm2 at 12.1T and 4.2K. Evidential substitution of carbon into the MgB2 changed the electron scattering and therefore raised the Bc2 up to 12T at 10K. Systematic investigation on the influence of the heat treatment showed that, although an interfering Fe2B reaction layer was formed, an excellent Jc of 104A∕cm2 at 14.3T and 4.2K was achieved. |
---|---|
ISSN: | 0003-6951 1077-3118 |
DOI: | 10.1063/1.2773942 |