Reduction of the residual compressive stress of tetrahedral amorphous carbon film by Ar background gas during the filtered vacuum arc process

Tetrahedral amorphous carbon (ta-C) film was prepared by the filtered vacuum arc process with Ar background gas. The residual compressive stress of the film decreased significantly as the Ar flow rate increased, whereas negligible change in the mechanical properties was observed. Structure analysis...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of applied physics 2007-01, Vol.101 (2)
Hauptverfasser: Kim, Tae-Young, Lee, Churl Seung, Lee, Young Jin, Lee, Kwang-Ryeol, Chae, Keun-Hwa, Oh, Kyu Hwan
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Tetrahedral amorphous carbon (ta-C) film was prepared by the filtered vacuum arc process with Ar background gas. The residual compressive stress of the film decreased significantly as the Ar flow rate increased, whereas negligible change in the mechanical properties was observed. Structure analysis by Raman spectroscopy, near edge x-ray absorption fine structure, and electron spin resonance spectra revealed a close relationship between the residual compressive stress and the bond distortion that invokes paramagnetic defects or unpaired π electrons. These results demonstrate that the stress reduction can occur by relaxation of the distorted or twisted atomic bonds at the same fraction of sp3 hybridized bonds, which enhances the stability of the ta-C coating without deterioration in the advantageous properties. The effect of Ar background gas is discussed in terms of the increased ion population of low kinetic energy in the plasma beam.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.2408385