Investigation of ultrafast demagnetization and cubic optical nonlinearity of Ni in the polar geometry
Femtosecond optical pump-probe experiments were performed upon a Ni(720 Å)/Si(100) sample in the polar geometry with the pump beam close to normal incidence. A signal due to the ultrafast demagnetization effect was observed when the pump pulse was linearly polarized. When the pump was elliptically p...
Gespeichert in:
Veröffentlicht in: | Journal of applied physics 2004-06, Vol.95 (11), p.7441-7443 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Femtosecond optical pump-probe experiments were performed upon a Ni(720 Å)/Si(100) sample in the polar geometry with the pump beam close to normal incidence. A signal due to the ultrafast demagnetization effect was observed when the pump pulse was linearly polarized. When the pump was elliptically polarized, additional peaks were observed at zero time delay, resulting from the specular inverse Faraday effect (SIFE) and the specular optical Kerr effect (SOKE). By comparing measurements made with different pump helicities, the SIFE and SOKE peaks and the demagnetization signal were found to superpose in a linear fashion. From the dependence of the peak height upon the pump polarization, values of χxxyy=(1−3i)×10−10 rad cm3 erg−1 and χxyyx=(−9+2i)×10−12 rad cm3 erg−1 were deduced for the nonvanishing components of the local cubic susceptibility tensor. For applied fields less than the saturation value, the sudden reduction of the thin film demagnetizing field leads to an imbalance of the torques acting upon the magnetization, causing it to precess. |
---|---|
ISSN: | 0021-8979 1089-7550 |
DOI: | 10.1063/1.1687538 |