Polar solvent-free room temperature synthesis of CsPbX 3 (X = Br, Cl) perovskite nanocubes

Conventionally, colloidal lead halide perovskite nanocubes have been synthesized by the hot-injection or ligand-assisted reprecipitation (LARP) methods. We herein demonstrate a polar solvent-free room temperature method for the synthesis of CsPbX 3 (X = Br, Cl) nanocubes. In addition to the commonly used ligand pair of oleylamine and oleic acid, guanidinium (GA) has been used to passivate the surface of the nanocrystals. Our study demonstrates that GA inhibits the formation of low dimensional structures such as nanowires and nanoplatelets and further supports the formation of perovskite nanocubes. In fact, GA diminishes the restricted monomer-addition effect of long-chain oleylammonium (OLAM) ions to the nanocrystal. We show that above a critical GA/OLAM molar ratio, the synthesis yields homogeneous CsPbX 3 (X = Br, Cl) nanocubes. Importantly, we observe the nucleation and growth kinetics of the GA-assisted CsPbBr 3 nanocube formation by using in situ absorption and photoluminescence (PL) measurements. Small nanocrystals with an excitonic absorption peak at around 435 nm and photoluminescence (PL) maxima at 447 nm were nucleated and continuously shifted to longer wavelengths during the growth period. Crucially, our method allows the synthesis of CsPbCl 3 nanocubes at room temperature without using polar organic solvents. The synthesized CsPbBr 3 , CsPb(Cl 0.5 Br 0.5 ) 3 , and CsPbCl 3 nanocubes have PL peaks at 508 nm, 443 nm, and 405 nm, photoluminescence quantum yields (PLQY) of 85%, 58% and 5%, and lifetimes of 18.98 ns, 18.97 ns, and 14.74 ns, respectively.