Enhanced cyclability of Li-O 2 batteries with cathodes of Ir and MnO 2 supported on well-defined TiN arrays

The cycling stability of Li-O batteries has been impeded by the lack of high-efficiency, and durable oxygen cathodes for the oxygen-reduction reaction (ORR) and the oxygen-evolution reaction (OER). Herein we report a novel TiN nanorod array-based cathode, which was firstly prepared by growing a TiN...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Nanoscale 2018-02, Vol.10 (6), p.2983-2989
Hauptverfasser: Leng, Limin, Li, Jing, Zeng, Xiaoyuan, Tian, Xinlong, Song, Huiyu, Cui, Zhimin, Shu, Ting, Wang, Haishui, Ren, Jianwei, Liao, Shijun
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The cycling stability of Li-O batteries has been impeded by the lack of high-efficiency, and durable oxygen cathodes for the oxygen-reduction reaction (ORR) and the oxygen-evolution reaction (OER). Herein we report a novel TiN nanorod array-based cathode, which was firstly prepared by growing a TiN nanorod array on carbon paper (CP), and then followed by depositing MnO ultrathin sheets or Ir nanoparticles on the TiN nanorods to form well-ordered, three-dimensional (3D), and free-standing structured cathodes: TiN@MnO /CP and TiN@Ir/CP. Both cathodes exhibited good specific capacity and excellent cycling stability. Their specific discharge capacities were up to 2637 and 2530 mA h g , respectively. After 200 cycles for 2000 h at a current density of 100 mA g , no obvious decays were observed for TiN@MnO /CP and TiN@Ir/CP cathodes, while significant decreases were observed after the 80 and 30 cycles for the Pt/C and TiN/CP cathodes, respectively. Such high performance can be ascribed to the 3D array structure with enough microspace and high surface area, which facilitated the high dispersion of active components and prevented the formation of large/irreversible Li O .
ISSN:2040-3364
2040-3372
DOI:10.1039/C7NR08358K