Research on erosion wear behavior of NiTi alloy coating fabricated via high-frequency induction heating technology

NiTi alloy is widely used in extreme working conditions due to its pseudoelasticity, shape memory effect and wear resistance. In this study, the NiTi alloy coating (Ni49.8Ti50.2 (at%)) was fabricated by high-frequency induction heating. The coating was well-formed on the surface of cemented carbide YG8 and converted to crystalline after aging treatment. The results of 70h erosion wear experiments carried on the rotary erosion wear test device showing that the erosion wear amount of the coating was reduced by 93 % compared with that of YG8, resulting from the deformation recovery effect. Moreover, the main erosion wear mechanism of the coating was micro-cutting and ploughing. This study can provide technical support and theoretical basis for preparing of NiTi alloy coating and erosion wear resistance. •The coating was prepared using high-frequency induction heating technology.•The coating has better erosion and wear resistance at different test temperatures.•The ability of recoverable deformation improves the erosion wear resistance of the coating.