Investigation of the effects of scale and cure environment on the properties of vinyl ester polymer
This work involves the study of the cure kinetics of a commercial bisphenol-epoxy vinyl ester resin as a function of sample thickness and environment atmosphere. It has been previously suggested that cured vinyl ester polymer is a diphasic material consisting of a lower Tg styrene phase and a higher...
Gespeichert in:
Veröffentlicht in: | Polymer (Guilford) 2024-07, Vol.307, p.127344, Article 127344 |
---|---|
Hauptverfasser: | , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | This work involves the study of the cure kinetics of a commercial bisphenol-epoxy vinyl ester resin as a function of sample thickness and environment atmosphere. It has been previously suggested that cured vinyl ester polymer is a diphasic material consisting of a lower Tg styrene phase and a higher Tg vinyl ester phase. The cure kinetics of each phase have been observed to have a significant effect on the thermal properties of the system, such as the degree of crosslinking, glass transition temperature and final conversion. DSC, DMA and FTIR were employed to characterize two vinyl ester resin systems and study the material property transferability from macroscale to microscale. The effect of reduced styrene content on resin curing and polymer thermal behaviour was studied. The effect of oxygen interaction during initial cure was investigated at both microscale and macroscale and found to have a significant effect on final polymer performance.
[Display omitted]
•Vinyl ester polymer properties are dependent on the polymerisation scale.•Vinyl ester polymer properties are affected by oxygen presence during polymerisation.•Vinyl ester polymer microstructure is dependent on the resin styrene content. |
---|---|
ISSN: | 0032-3861 1873-2291 |
DOI: | 10.1016/j.polymer.2024.127344 |