Structure, morphology and magnetic properties of flowerlike γ-Fe2O3@NiO core/shell nanocomposites synthesized from different precursor concentrations

Flowerlike γ-Fe2O3@NiO Core/Shell Nanocomposites. [Display omitted] •Flowerlike γ-Fe2O3@NiO core/shell nanocomposites are synthesized by the two-step method.•Their structure and morphology can be controlled by tuning the precursor concentration.•NiO shells are built of many irregular nanosheets which are wrapt around the surface of γ-Fe2O3 core.•Small exchange bias is because of the NiO nanosheets with disordered orientations and does not form a complete coating. The flowerlike γ-Fe2O3@NiO core/shell nanocomposites are synthesized by the two-step method. Their structure and morphology can be controlled by tuning the precursor concentration. Microstructural analysis reveals that all the samples have distinct core/shell structure without impurities, and the NiO shells are built of many irregular nanosheets which enclose the surface of γ-Fe2O3 core. As the precursor concentration decreases (i.e., more NiO content), the NiO grain grows significantly, and the thickness of NiO shells increases. Magnetic experiments are performed to analyze the influences of different microstructures on magnetic properties of samples and we have the following two results. First, at 5 K, along with increasing thickness of NiO shell, the saturation magnetization increases, while the residual magnetization decreases slightly. Second, the hysteresis loops under cooling field demonstrate that the value of exchange bias effect fluctuates between 13 Oe and 17 Oe. This is mainly because of the NiO shell that (i) is composed of irregular nanosheets with disordered orientations, and (ii) does not form a complete coating around γ-Fe2O3 core.