Magnetic properties and large low-field magnetocaloric effect of RFe2Si2 (R = Ho, Tm) compounds

•RFe2Si2 (R = Ho, Tm) intermetallic compounds were successfully synthesized.•Ultra-low working temperature and large low-field magnetocaloric effect were obtained.•Good thermal and magnetic reversibility were confirmed based on the analysis of transition.•RFe2Si2 (R = Ho, Tm) compounds show potential applications on low-temperature magnetic cooling. Nowadays, magnetic refrigerant technology has drawn much attention for its environmental friendliness. Those magnetic materials possessing giant low-field magnetocaloric effect (MCE) performance are of great importance for practical applications, especially at low temperatures. Herein, we present a detailed study on polycrystalline magnetocaloric compounds HoFe2Si2 and TmFe2Si2. HoFe2Si2 exhibits a transition from antiferromagnetic to paramagnetic phase at 2.2 K, while no long-range magnetic ordering is observed in TmFe2Si2 even temperature down to 2 K. For both compounds, they showed large low-field magnetic entropy change (−ΔSM) with the peak values of 10.6 and 7.9 J kg−1 K−1 under field change of 0–2 T for HoFe2Si2 and TmFe2Si2, respectively, which is comparable or even larger than some low-temperature magnetocaloric materials. In addition, the characteristic of second-order magnetic transitions of both compounds were confirmed on basis of Arrott plots and mean-field theory criterion. The low magnetic ordering temperatures, large low-field MCE performance along with the feature of second order phase transition for HoFe2Si2 and TmFe2Si2 indicate that both compounds are promising candidate for magnetic refrigerant materials at liquid helium temperature.