Efficient separation and purification of indium and gallium in spent Copper indium gallium diselenide (CIGS)

Copper indium gallium diselenide (CIGS), is a promising commercial thin-film solar cell, and its disposal after scrapping and recycling critical metals has attracted tremendous attention since CIGS can be considered an important type of urban mining. The main phase of spent CIGS is selenide, which is a hazardous contaminant that may have a potential impact on the environment and human body. In our previous study, selenium and copper in spent CIGS separated efficiently, while more scarce metals: indium and gallium were obtained in the form of mixed indium gallium oxide (IGO). Therefore, in this study, the separation and purification of indium and gallium was investigated in detail. The solution chemical behavior shows that the dissolution of indium gallium oxide (IGO) in an alkaline environment was significantly different. Selective alkali leaching is feasible to separate indium and gallium effectively. The process realized 97.26% gallium leaching out, while that of indium was 3.37%. Moreover, the mechanism of the leaching process and the removal of copper impurities were explored, with further purification, indium and gallium were obtained in the form of relatively pure indium oxide (96.04%) and gallium oxide (99.83%), respectively. This study will provide guidance for the recycling of critical metals from secondary waste. [Display omitted] •An effective process for indium gallium separation in spent CIGS was developed.•Theoretical analysis of indium gallium separation in an alkaline system was analyzed.•The high purity products were obtained after purification.•Indium and gallium were recovered as pure In2O3 and Ga2O3 respectively.