Surface-initiated polymerization of PVDF membrane using amine and bismuth tungstate (BWO) modified MIL-100(Fe) nanofillers for pesticide photodegradation

Pirimicarb as a pesticide is used to control the aphids in the agriculture field; however, it affects the groundwater ecosystem by leaching through the soil profile. The post-synthetic amine and BWO modified MIL-100 (Fe) nanofillers were synthesized. The photocatalytic property of amine-functionalized and BWO@MIL-100(Fe) nanofillers was confirmed by the lesser bandgap energy than the unmodified MIL-100 (Fe) nanofiller. Herein, we constructed a nanofillers grafted PVDF membrane via in-situ polymerization technique for the pirimicarb reduction and photodegradation. Furthermore, the nanofiller's grafted membranes were characterized by FESEM, XRD, FTIR, and contact angle analysis. The carboxylic acid peak was observed on the FTIR which demonstrated the PAA grafted on the membrane surface and similar crystalline peaks evident that the nanofillers were grafted on the membrane surface. Furthermore, surface morphology studies have exhibited the dispersion of nanofillers and enhanced microvoids in the cross-section of the membrane. The decrease in the water contact angle of the membrane depicted the improved antifouling properties and surface energy. The nanofiller's grafted membranes have shown higher hydrophilicity correlated well with the enhanced pure water flux in the order M4 > M5 > M2 > M3 > M6 > M7 compared to the neat membrane (M1). In BWO@MIL-100(Fe) membrane has shown a higher permeate flux (25.99 L m−2.h−1) than the neat PVDF membrane. The BWO@MIL-100(Fe) grafted PVDF membrane has also shown excellent pirimicarb photodegradation of 81% at pH 5. The proposed MIL-100 (Fe) and bismuth tungsten nanocomposite will pave the way for the different MOF-based photocatalytic materials for membrane-based pesticide degradation. [Display omitted] •NH2 and BWO modified MIL-100(Fe) nanofillers were synthesized by solvothermal method.•Nanofillers were grafted on the PVDF membrane via In-situ polymerization.•BWO@MIL-100(Fe) membrane has shown permeate flux (25.99 L m−2.h−1) and rejection of 84%.•The BWO@MIL-100(Fe) grafted membrane has shown 81% of pirimicarb degradation.