The effect of the Al 2 O 3 content and basicity (the molar ratio of MgO to SiO 2 ) on the viscosity of a SiO 2 –MgO–FeO–Al 2 O 3 –CaO slag was studied to fully understand the smelting process of the ferronickel alloy. Experimental results show that the slag is a mixture of liquid and solid phases at...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of iron and steel research, international international, 2020-12, Vol.27 (12), p.1400-1406
Hauptverfasser: Chen, Yong-feng, Lv, Xue-ming, Pang, Zheng-de, Lv, Xue-wei
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The effect of the Al 2 O 3 content and basicity (the molar ratio of MgO to SiO 2 ) on the viscosity of a SiO 2 –MgO–FeO–Al 2 O 3 –CaO slag was studied to fully understand the smelting process of the ferronickel alloy. Experimental results show that the slag is a mixture of liquid and solid phases at the experimental temperature. The viscosity decreased as the basicity increased and increased as the Al 2 O 3 content increased. To determine the effect of the Al 2 O 3 content and basicity on the structure of the molten slag, Raman spectroscopy was performed on the slag sample, which was quenched from the high temperature with water. The Raman spectra showed that the fractions of the polymerization structural units decreased significantly as the basicity of the slag increased, resulting in a decrease in the apparent viscosity. However, Al 2 O 3 acts as a network former in the slag system, thereby making the slag structure further polymerized and increasing the viscosity.