Synthesis and characterization of hydroxyapatite powder from natural Camelus bone

This study aims to synthesize and characterize hydroxyapatite (HAp) bio-ceramic powder. Calcination treatment was applied to produce the hydroxyapatite powders from Camelus bone as an eco-friendly and inexpensive source. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, field emission scanning electron microscopy (FESEM) with energy-dispersive X-ray spectrometry (EDS), and atomic force microscopy (AFM) were carried out to characterize the synthesized powder. XRD results showed that material obtained at calcination temperature (1000 °C) is a HAp according to (ICDD 00-024-0033) pattern in a 1.6557 Ca/P molar ratio and the chemical composition is Ca 5 (PO 4 ) 3 (OH). The FTIR and Raman spectra confirm the formation of HAp by the presence of peaks corresponding to (PO 4 ) 3− and OH − groups, which are of great importance in HAp molecules. The experimental results of FESEM and AFM showed that the shape of the hydroxyapatite particles was irregular with the particle size ranging from 79 nm to 0.9 μm.