Corrosion behavior of thermal-sprayed WC cermet coatings in SO4^2- environment

A series of the electrochemical and long-term corrosion tests was carried out in a 3.5 wt% Na2SO4 solution on thermal-sprayed WC-17Co and WC-10Co-4Cr cermet coatings in order to examine the effect of composition of binder materials on the corrosion behavior. The results reveal that the overall corrosion resistance of the WC-17Co coating is inferior to that of the WC-Co-Cr coatings due to the corrosion of binder materials which induce WC particles to fall off. CoO and WO3 oxide films form on the surface of WC-17Co coating in Na2SO4 solution electrochemical corrosion process, which will protect the coating in the process of corrosion. Cr2O3 oxide film formed on the WC-10Co-4Cr coating surface has a strong hindered role to corrosion. The corrosion mechanism of WC-17Co coating in Na2SO4 solution is entire corrosion of Co matrix, while it is film-hole corrosion mechanism for WC-10Co-4Cr coating.