Effect of the Heat Treatment on the Corrosion Resistance of Duplex Stainless Steels

Duplex stainless steels (DSS) are biphasic austenitic-ferritic steels in which the best combination of mechanical and corrosion resistance properties is achieved for an almost equal volume fraction of the phases. In this work, the effect of secondary phases precipitation on the corrosion resistance of four DSS grades (2101, 2304, 2205 and 2507), after isothermal aging in the critical temperature range 750-900 °C, was studied. The corrosion resistance was investigated by potentiodynamic polarization tests in both 0.6 M NaCl solution (pH 7) and in an acid chlorinated solution (pH 3) at room temperature. Moreover, the critical pitting temperature was determined according to ASTM G150. The results showed that secondary phases precipitation mainly influenced the resistance to corrosion of the lean duplex grades.