Thermodynamic properties of graphite-like nanostructures prepared by thermobaric treatment of fullerite C60

Temperature dependences of the heat capacities of disordered graphite-like nanostructures prepared by the thermobaric treatment of fullerite C 60 ( p = 2 and 8 GPa, T = 1373 K) were measured in the temperature ranges from 7 to 360 K in an adiabatic vacuum calorimeter and from 330 to 650 K in a differential scanning calorimeter. At T < 50 K, the dependences obtained were analyzed using the Debye theory of the heat capacity of solids and its multifractal version. The fractal dimensions D were determined and some conclusions on the heterodynamic character of the structures studied were made. The thermodynamic functions C p o T ), H o ( T ) − H o (0), S o ( T ) − S o (0), and G o ( T ) − H o (0) were calculated in the temperature range from T → 0 to 610 (650) K. The thermodynamic properties of the graphite-like nanostructures studied and some carbon allotropes were compared. The standard entropies of formation Δ f S o of the graphite nanostructures studied and diamond were calculated along with the standard entropies of the reactions of their synthesis from the face-centered cubic phase of fullerite C 60 and their interconversions at T = 298.15 K.