Anion receptor-coated separator for lithium-ion polymer battery

Anion receptor-coated separators were prepared by coating poly(ethylene glycol) borate ester (PEGB) as an anion receptor and poly(vinyl acetate) (PVAc) as a good adhesive material towards electrodes onto microporous polyethylene (PE) separators. Gel polymer electrolytes were fabricated by soaking them in an liquid electrolyte, 1 M LiPF 6 in EC/DEC/PC (30/65/5, wt.%). As the weight ratio of PEGB to PVAc in a coating layer increased, gel polymer electrolytes showed higher cationic conductivity and electrochemical stability. The cationic conductivity and electrochemical stability of the gel polymer electrolyte based on coated separator with PVAc/PEGB (2/5, weight ratio) could reach 2.8 × 10 –4 S cm –1 and 4.8 V, respectively. Lithium-ion polymer cells (LiCoO 2 /graphite) based on gel polymer electrolytes with and without PEGB were assembled, and their electrochemical performances were evaluated.