Influence of hydrothermal modification of fibers on some physical and mechanical properties of medium density fiberboard (MDF)

Any treatment of fibers can influence properties of medium density fibreboard (MDF). In this research, the effects of hydrothermal treatment on physical and mechanical properties of MDF were studied. Industrial fibers were hydrothermally treated in a stainless steel reactor at 120, 150 and 180 °C for 0, 30 and 90 min as holding time. Test boards were made based on 0.7 g/cm 3 target density, with 10 mm thickness under a pressure of 30 bar and at a temperature of 170 °C and a press time of 10 min. The boards were tested for internal bonding (IB), moduli of elasticity (MOE) and rupture (MOR), thickness swelling and water absorption. Results showed that the water absorption was not affected by the hydrothermal treatment; while the thickness swelling was improved and the boards became dimensionally stable. The MOE was slightly reduced due to the hydrothermal treatment. The MOR and the IB were significantly decreased by the hydrothermal treatment.