Infrared absorption spectra of some Manganese Dioxide Modifications and their thermal products

The infrared absorption spectra of α‐, β‐, γ‐ and δ‐ MnO2 prepared by different methods, were measured and discussed. It was found that the ratio of absorbancies of the bands at 595 ± 20 cm−1 und 535 ± 20 cm−1 (φ) is related to the amorphous content. Each preparation is characterized by a certain value of φ. The mode of change of φ as a result of heating the different preparations is discussed. Infrared spectra help in differentiating α‐, γ and δ‐MnO2 on the one hand, and β‐MnO2 on the other, and in indicating the transformation of γ‐into β‐MnO2 by heating the former at 450 °C. α‐, β‐, γ und δ‐MnO2 wurden nach verschiedenen Methoden dargestellt und ihre IR‐Spektren aufgenommen und verglichen. Es zeigte sich. Daß das Verhältnis der Absorption der Banden bei 595 ± 20 cm−1 und 535 ± 20 cm−1 (φ) abhängt vom amorphen Anteil. Jede Charge wird durch einen bestimmten Wert von φ charakterisiert. Die Art der Ånderung von φ durch Tempern der Proben wird diskutiert. Die IR‐Spektren erlauben eine Unterscheidung von α‐, γ‐ und δ‐MnO2 einerseits und β‐MnO2 andererseits; auch ist der Übergang der γ‐ in die β‐Form beim Tempern bei 450°C zu erkennen.