Melting equilibria in the iron‐rich corner of the Fe‐Ni‐Mo system

Isothermal holding tests were carried out in the Fe‐Ni‐Mo system in the two‐phase region between the liquidus (melt) and the solidus (crystal). The δ and γ liquidus surfaces in the iron‐rich corner of the Fe‐Ni‐Fe3Mo2‐NiMo subsystem, as well as the position of the peritectic line situated between them, could be very accurately established by the experimentally determined isotherms. Based on these results and on the known liquidus lines in the three boundary binary systems, as well as on the known concentration fields of the Fe3Mo2‐NiMo solid solutions, the melting equilibria could be developed with sufficient accuracy in the entire subsystem. Im System Fe‐Ni‐Mo wurden isotherme Halteversuche im Zweiphasengebiet zwischen Schmelze und Kristall durchgeführt. Die Versuchsergebnisse legen die δ‐ und γ‐Liquidusflächen in der eisenreichen Ecke des Teilsystems Fe‐Ni‐Fe3Mo2‐NiMo durch Isothermen und die Position der zwischen ihnen liegenden peritektischen Linie, durch die Schnittpunkte der Isothermen, sehr genau fest. Aufbauend auf diesen Ergebnissen und den bekannten Liquiduslinien der drei Randsysteme sowie den Konzentrationsbereichen der Fe3Mo2‐NiMo‐Mischkristalle, lassen sich die Schmelzgleichgewichte des gesamten Teilsystems mit genügender Genauigkeit entwickeln.