Resistance of 9–20%Cr‐steels against metal dusting

The metal dusting resistance of various 2¼ Cr to 20%Cr steels has been tested in flowing CO‐H2‐H2O atmospheres at 525, 560, 600 and 650°C. For the 2¼Cr‐steel immediately a constant rate of metal wastage is reached, for the high alloy steels the approach to this rate where all surface area is attacked, is more or less retarded by an oxide layer. The formation of a protective Cr‐rich oxide layer is favoured by a high Cr‐content of the steels, by the ferritic structure, by a fine‐grained microstructure, by surface working and by high temperatures – these factors hinder or suppress metal dusting, whereas low Cr‐concentration, austenitic structure, coarse‐grained microstructure, removal of surface deformation by etching and a critical temperature of ≤ 600°C accelerate and enhance metal dusting. Die Beständigkeit von verschiedenen 2¼Cr‐ bis 20%‐Cr‐Stählen gegen Metal Dusting wurde in strömenden CO‐H2‐H2O‐Atmosphären bei 525, 560, 600 und 650°C geprüft. Für den 2¼Cr‐Stahl wird unmittelbar die konstante Geschwindigkeit des Metallabtrags erreicht, für die höherlegierten Stähle erfolgt das Erreichen dieser Geschwindigkeit, bei der die gesamte Oberfläche angegriffen wird, mehr oder weniger durch eine Oxidschicht verzögert. Die Bildung einer schützenden, Crreichen Oxidschicht wird durch hohen Cr‐Gehalt der Stähle, durch ferritisches Gitter, durch feinkristallines Gefüge, durch Oberflächenverformung und durch hohe Temperaturen begünstigt – diese Faktoren behindern oder unterdrücken das Metal Dusting, während eine niedrige Cr‐Konzentration, austenitisches Gitter, grobkörniges Gefüge, Entfernen der oberflächenverformten Zone durch Ätzen und kritische Temperaturen unterhalb ≤ 600°C das Metal Dusting begünstigen und beschleunigen.