Charge Conversion of Chromium and Vanadium Ions in CdF 2

The optical absorption spectra of CdF 2 :Cr crystals show that the charge conversion Cr 3+ ⟷ Cr 2+ takes place completely and reversibly by heating in Cd and halogen vapour, respectively. The correlated investigation of optical and EPR spectra of CdF 2 :V crystals suggest that the optical spectrum after heating in halogen vapour is caused by small precipitated particles of VF 3 whereas the EPR spectrum is due to V 3+ on Cd sites. Thus the charge conversion V 3+ ⟷ V 2+ can be investigated only with the EPR spectra showing that the conversion V 3+ → V 2+ depends on the total concentration of trivalent ions on Cd sites. Die an CdF 2 : Cr‐Kristallen gemessenen optischen Absorptionsspektren zeigen, daß die Ladungsumwandlung Cr 3+ ⟷ Cr 2+ vollständig und reversibel möglich ist durch Temperung im Cd‐ bzw. Halogendampf. Die parallel durchgeführten Untersuchungen der optischen und EPR‐Spektren von CdF 2 :V‐Kristallen weisen darauf hin, daß das optische Absorptions‐spektrum nach Temperung im Halogendampf durch kleine Partikel von ausgeschiedenem VF 3 verursacht wird, während die EPR‐Spektren durch V 3+ Ionen auf Cd‐Plätzen ver. ursacht werden. Die Ladungsumwandlung V 3+ ⟷ V 2+ kann daher nur mit Hilfe der EPR‐Spektren untersucht werden. Dabei wurde gefunden, daß die Umwandlung V 3+ → V 2+ von der Gesamtkonzentration dreiwertiger Ionen auf Cd‐Plätzen abhängt.