Mixed electronic-ionic conduction in glasses of the AgI-Ag2O-V2O5-P2O5 system

The glasses of the AgI‐Ag2O‐V2O5‐P2O5 system exhibiting mixed electronic‐ionic conduction were synthesized. Both components of the total conductivity s̀tot = s̀e + s̀i were separated by means of the impedance/admittance spectroscopy method. Temperature dependencies of electronic (e) and ionic (i) conductivities as well as corresponding transference numbers te and ti were investigated. The values of activation energies Ee and Ei for both conduction processes were determined. It was demonstrated that via a continuous modification of chemical composition of the glasses it was possible to obtain a continuous transition of their electric conduction from almost pure electronic through mixed electronic‐ionic to purely ionic one. Les verres du système AgI‐Ag2O‐V2O5‐P2O5 conducteurs mixes électroniques‐ioniques ont été préparés. On a séparé les deux composantes (électronique et ionique) de la conductivité totale s̀tot = s̀e + s̀i par la méthode de la spectroscopie impédance/admittance. Les conductivités électronique, ionique avec leurs numéros de transférence te et ti ont été examinées en fonction de la température. Les valeurs d'énergies d'activation de deux processus ont été déterminées. On a démontré que par la modification contrǒlée de la composition chimique des verres, on peut obtenir la transition continue de la conductivité électronique à la conductivité ionique passant par la région de la conductivité mixte électronique‐ionique.