Short-range reordering of heavy interstitials in Ta, Nb, and Fe during relaxation and static strain aging

Using isothermic relaxation tests and internal friction, the mechanism of a Snoek type reordering of heavy interstitials (oxygen, carbon, nitrogen) in tantalum, niobium, and iron is studied. The kinetics and the amplitude of the stress relaxation conform to the general theory of the inelastic dipole due to Berry and Nowick. In an identical temperature range and on the same solid solutions, the effect of static strain aging is investigated on the yield point effect represented by the parameter Δσ/σ. It is shown that, in accordance with the Schoeck and Seeger model, the first period of aging is due to the reorientation at short distance of the interstitials in the dislocation stress field. In fact, the identification of the two phenomena leads to the relation Δσ(t)/σ = α Δs(t), with α close to the unity, which is in accordance with experiments. Mittels isothermischer Relaxation und innerer Reibung wird der Mechanismus der Snoek‐Umordnung von schweren Zwischengitterstörstellen (Sauerstoff, Kohlenstoff, Stickstoff) in Tantal, Niob und Eisen, untersucht. Die Kinetik und die Amplitude der Spannungsrelaxation stimmt mit der allgemeinen Theorie anelastischer Dipole von Berry und Nowick überein. In einem identischen Temperaturbereich und an den gleichen festen Lösungen wird der Einfluß einer statischen Spannungsalterung auf den Fließpunkt, dargestellt durch den Parameter Δσ/σ untersucht. Es wird gezeigt, daß in Übereinstimmung mit dem Model1 von Schoeck und Seeger, der erste Abschnitt der Alterung durch eine Reorientierung innerhalb eines kleinen Abstands von den Zwischengitterstörstellen im Spannungsfeld der Versetzung hervorgerufen wird. Tatsächlich führt die Identifizierung der beiden Phänomene zu der Beziehung Δσ(t)/σ = α Δs(t), wobei α nahe bei eins liegt in Übereinstimmung mit Experimenten.