Surface ionic conductivity, lattice disorder, and space charge region in thin silver bromide layers

Carefully controlled conditions of evaporation allow the preparation of epitaxial layers of pure AgBr. The temperature dependence of the conductivity of layers with varying thickness is measured. This in principle makes possible the splitting of the conductance into surface and bulk components. The bulk conductivity of the layers is found to be practically identical with that of pure large single crystals of AgBr, which until now has not been observed. For the first time considerable surface conductance is directly observed not only for {111} but for {200} layers too. All parameters characterizing the Frenkel disorder in the subsurface region are evaluated from 150 °C down to room temperature. Dünne Epitaxieschichten aus reinem Silberbromid werden unter sorgfältig kontrollierten Bedingungen hergestellt. Die Temperaturabhängigkeit der Leitfähigkeit wird für verschiedene Schichtdicken gemessen. Dies erlaubt im Prinzip, die Leitfähigkeit in eine Oberflächen‐ und eine Volumenkomponente zu trennen. Es wird gefunden, daß die Volumenleitfähigkeit der Schichten mit der von großen, reinen Silberbromideinkristallen identisch ist, was bis jetzt noch nicht beobachtet wurde. Zum ersten Mal wird eine beträchtliche Oberflächenleitfähigkeit nicht nur für die {111}‐sondern auch für die {200}‐Schichten direkt festgestellt. Alle Parameter, die die Frenkel‐Fehlordnung in den oberflächennahen Gebieten charakterisieren, werden in einem Temperaturintervall von 150 °C bis Zimmertemperatur ausgewertet.