Energy distribution of electrons field-emitted from cadmium sulphide

A retarding potential analyser was used to investigate the energy distribution of electrons field‐emitted from cadmium sulphide. The analyser was thoroughly investigated theoretically and tested by obtaining accepted values for the energy distribution from tungsten. A somewhat unusual secondary electron correction procedure was used. The results from cadmium sulphide were found to be of two kinds: with a single peak or with two peaks. The latter occurred only from insufficiently cleaned tips. The experimental distributions for clean CdS were of ≈0.6 eV half‐width, which is considerably broader than predicted by theory. The width of the experimental distributions is a function of the emitted current density but the limiting value of the width could always be obtained. Some suggestions for a theoretical interpretation are put forward. Ein Gegenfeldanalysator wurde zur Messung der Energieverteilung von aus CdS feldemittierten Elektronen benutzt, wobei der Analysator theoretisch untersucht und durch Messungen an Wolfram, welche die üblichen Resultate ergaben, überprüft wurde. Zur Sekundärelektronenkorrektur wurde eine neue Methode benutzt. Die Messungen an CdS ergeben zwei Kurventypen, mit einem Maximum order mit zwei Maxima. Die zweite Art wird nur an ungenügend gesäuberten Emissionsspitzen beobachtet. Die experimentellen Energieverteilungen für sauberes CdS haben eine Halbwertsbreite von etwa 0,6 eV, sind also wesentlich breiter als theoretisch vorausgesagt. Die Breite der experimentellen Verteilungen steigt mit dem Emissionsstrom, jedoch kann die Mindestbreite immer ermittelt werden. Es werden einige Vorschläge zur theoretischen Deutung der Ergebnisse gemacht.