Influence of additives on the crystal structure and melting behavior of poly(ethylene-2,6-naphthalene dicarboxylate)

The influence of additives on the crystal modification and melting behavior of poly(ethylene‐2,6‐naphthalene dicarboxylate) (PEN) was investigated with wide‐angle X‐ray diffraction and differential scanning calorimetry (DSC). The addition of a nucleating promoter, Ceraflour 993, had no effect on the crystal modification and melting behavior of PEN crystallized under all chosen experimental conditions. However, the addition of a nucleating agent, sodium benzoate (SB), did affect the crystal modification and melting behavior of PEN when PEN/SB was crystallized at a higher temperature, but not at a lower temperature. A mixture of α and β modifications of PEN was obtained, and an overlapped dual melting peak was observed in DSC curves when PEN was crystallized at a higher temperature in the presence of SB, instead of a single crystal form and a single melting peak for the crystallization of pure PEN. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 296–301, 2004