Synthesis and solution properties of poly(methacrylate)s with semipolar structures on the side chains

Poly{2‐(N,N‐dimethylamino)ethyl methacrylate [poly(DMMA)]}, which was prepared by radical polymerization initiated with dimethyl 2,2‐azobis(2‐methylpropionate), was reacted with hydrogen peroxide, diethyl sulfate, and chloroacetic acid to yield poly[N,N‐dimethyl‐N‐(2‐methacryloyloxyethyl)amine N‐oxide] [poly(DMANO)], poly[N‐ethyl‐N,N‐dimethyl‐N‐(2‐methacryloyloxyethyl)ammonium ethyl sulfate] [poly(EDMES)], and poly[N,N‐dimethyl‐N‐(2‐methacryloyloxy)ethylammonioacetate] [poly(DMEAA)] as ion‐containing water‐soluble polymers, respectively. The solution properties of these charged polymers were compared via the reduced viscosities of these three charged polymers in aqueous solutions as a function of the concentration. Poly(EDMES) showed typical polyelectrolyte behavior, and the other two polymers [poly(DMANO) and poly(DMEAA)] exhibited antipolyelectrolyte behavior. Furthermore, the antipolyelectrolyte behavior was different for poly(DMANO) and poly(DMEAA); that is, poly(DMANO) was less dependent on small electrolytes. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 129–141, 2005 Three charged polymers—poly[N,N‐dimethyl‐N‐(2‐methacryloyloxyethyl)amine N‐oxide] [poly(DMANO)], poly[N‐ethyl‐N,N‐dimethyl‐N‐(2‐methacryloyloxyethyl)ammonium ethyl sulfate] [poly(EDMES)],and poly[N,N‐dimethyl‐N‐(2‐methacryloyloxy)ethylammonioacetate] [poly(DMEAA)]—were prepared by the reaction of poly[2‐(N,N‐dimethylamino)ethyl methacrylate] with hydrogen peroxide, chloroacetic acid, and diethyl sulfate, respectively. Poly(EDMES) showed typical polyelectrolyte behavior, but the other two polymers [poly(DMANO) and poly(DMEAA)] exhibited antipolyelectrolyte behavior.