The Inhibition of the Iron Corrosion in aqueous solutions containing oxygen

The corrosion behaviour of iron and steel in aerated aqueous 0.5 M Na2SO4 solutions in the range 7 ≤ pH ≤ 9 was studied on rotating disc electrodes. The polarization curves measured cyclic voltammetrically or under steady‐state potentiostatic conditions show a membrane inhibition effect caused by the time‐dependent formation of three‐dimensional porous oxide layers on the electrode surface. In presence of the inhibitors hexane (1, 6) biphosphonic acid, sodium‐dihydrogenphosphate, Preventol VP OC 2003 and Aktiphos the inhibition effect is markedly enhanced leading to more homogeneous and compact protecting layers. Inhibierung der Korrosion von Eisen in wäßrigen, sauerstoffhaltigen Lösungen Das Korrosionsverhalten von Eisen und Stahl wurde in belüfteten, wäßrigen 0,5 m Na2SO4 Lösungen im Bereich 7 ≤ pH ≤ 9 an rotierenden Scheibenelektroden untesucht. Die zyklisch voltammetrischen oder potentiostatisch stationär gemessenen Polarisationskurven zeigen einen Membraninhibitionseffekt, der durch die zeitabhängige Bildung von dreidimensionalen, porösen oxidischen Deckschichten auf der Elektrodenoberfläche hervorgerufen wird. In Gegenwart der Inhibitoren Hexan(1, 6)‐biphosphonsäure, Natrium‐dihydrogenphosphat, Preventol VP OC 2003 und Aktiphos wird der Inhibitionseffekt infolge Bildung homogenerer und kompakterer Schutzschichten deutlich verstärkt.