Synthesis, Characterization and Catalysis of Ce-MCM-41

The cerium‐containing MCM‐41 (Ce‐MCM‐41) has been synthesized by direct hydrothermal method. The low‐angle XRD patterns revealed the typical five major peaks of MCM‐41 type hexagonal structures. The interplanar spacing d100 = 38.4 Å was obtained that can be indexed on a hexagonal unit cell parameter with ao = 44.3 Å which was larger than that of pure siliceous MCM‐41 (Si‐MCM‐41). Transmission electron micrograph shows the regular hexagonal array of uniform channel characteristics of MCM‐41. The BET surface area of Ce‐MCM‐41 was 840 m2/g, which is much reduced as compared to that of Si‐MCM‐41, with the pore size of 26.9 Å and mesopore volume of 0.78 cm3/g were measured by nitrogen adsorption‐desorption isotherm at 77 K. Along with the results, the synthesized Ce‐MCM‐41 exhibited a well‐ordered MCM‐41‐type mesoporous structure with the incorporation of cerium. Using Ce‐MCM‐41 as a support, the Rh (0.5 wt%) catalyst exhibited very high activity for the NO/CO reactions.