Tuning Electronic Structure of CuCo 2 O 4 Spinel via Mn‐Doping for Enhancing Oxygen Evolution Reaction

Cobalt‐based spinel oxide is a promising electrocatalyst for oxygen evolution reaction (OER) because of its low cost, excellent activity and stability. Herein, we designed the CuMn x Co 2 O 4 electrocatalyst with tunable electronic structure via Mn‐doping to enhance OER performance. Results showed that the CuMn 0.5 Co 2 O 4 catalyst prepared by calcined at 600°C exhibited high crystalline without impurity phase, and possessed the enhanced Co 2+ /Co 3+ ratio and high concentration of oxygen vacancies, which were facilitated to enhance OER performance. Electrochemical test results showed the CuMn 0.5 Co 2 O 4 catalyst had high OER performance with a low overpotential of 340 mV at the current density of 10 mA ⋅ cm −2 and a smaller Tafel slope of 69.8 mV ⋅ dec −1 . TOF and ECSA results illustrated that the more intrinsic catalytic activity on the CuMn 0.5 Co 2 O 4 catalyst. After 1000 cycles, the catalyst exhibited high stability with the 8 1.7 % of current retention rate. The OER activity enhancement mechanism of was further analyzed, which were mainly ascribed to the conversion of variable Co 2+ /Co 3+ and enhanced oxygen vacancies.