Preparation of Bi 2 O 3 @ PCPA‐KH590 /chloroprene composites with good mechanical properties under high‐filling

As a “green” radiation protection material with the potential to replace lead oxide, bismuth oxide has more research applications in the field of γ protection. However, due to their different surface properties, there are compatibility and interaction problems between metal oxides and rubber. To enhance the performance of bismuth oxide in neoprene, Bi 2 O 3 @PCPA‐KH590 was prepared by coating bismuth oxide with polyphenol/polyamine and grafting KH590 on the surface of bismuth oxide. This allows for creating more active sites with the help of polyphenol/polyamine, enabling KH590 to be grafted onto bismuth oxide particles. The S functional group on the silane coupling agent is then cross‐linked with the rubber substrate, enhancing the dispersibility of the bismuth oxide powder. This improvement not only improves the dispersibility of the bismuth oxide powder but also enhances the mechanical properties of the rubber composite material. Compared with pure CR, the mechanical properties of 60 wt% filler‐modified powder composites can still be maintained at a high level, with the tensile strength reaching 12.83 Mpa. In sum, the proposed method appears feasible for preparing highly filled radiation protection rubber‐based materials.